| Surface protective material for electronics/optical elements |
|
| E-MASK R•HR Series |
| E-MASK R-50EP/R-100/R-200/R-300/HR-6010/HR-6030 |
 |
| Low contamination type developed for surface protective
of electronic and optical parts. |
|
Outline |
|
| Nitto Denko E-MASK R Series is a series of
surface protective materials for optical parts. With unique adhesive synthetic
technology, it's suitable for surface protective of LCD polarizing film, hard
coat or non-glare acrylic plates, polycarbonate plates and polyester films during
transportation and processing. |
|
Features |
|
|
| • |
Changes in adhesive strength after lamination are extremely
small, ensuring easy peeling. |
| • |
Polyethylene film with excellent transparency for carrier
shows surface of the substrate without
removing the tape. |
| • |
Tape is pressure sensitive, and easily applied with a laminator. |
|
Applications |
|
|
| • |
Surface protective for optical film, such as polarizing film
(e.g. during LCD shipping) |
|
General properties |
|
| Item |
Thickness (mm)*1 |
Adhesive strength(N/20mm) *2 |
| E-MASK R-50EP |
0.060 |
0.10 |
| E-MASK R-100 |
0.065 |
0.30 |
| E-MASK R-200 |
0.065 |
0.50 |
| E-MASK R-300 |
0.070 |
0.80 |
| E-MASK HR-6010 |
0.063 |
0.50 |
| E-MASK HR-6030 |
0.070 |
0.90 |
|
[Test method]
*1:Nominal thickness
*2:Based on JIS Z-0237
Adherent: Acrylic plate, Tensile speed: 300mm/min, Peeling angle: 180° |
|
Precautions |
|
| • |
Avoid sunlight and store at room temperature and moderate humidity. |
| • |
Do not press too strong when applying. This may cause the end of the tape to peel. |
| • |
If applying to surfaces treated with machining oil, degrease the surface carefully. Any remains will be a cause for surface contamination or adhesive residue. |
| • |
For use under severe conditions, please test and evaluate the product thoroughly beforehand. |
• |
Painting, plating, etching, or gluing the surface after peeling the tape may be troublesome due to the small amount of residue of the adhesive. Please inspect under actual situations thoroughly before application. |
| • |
Painted boards, depending on conditions such as paint baking, may cause the tape to peel uneasily or peel off the paint together. Please evaluate thoroughly beforehand. |
| • |
Surface treated boards such as alumite, depending on treatment conditions, may show different properties (peeling) of SPV. Please evaluate thoroughly beforehand. |
| • |
Especially for applications against natural substrate (marble stone, lumber, et al.) please contact our sales representative in charge. |
| • |
The above datasheet is a sample observation value under certain testing conditions, not guaranteed performance. |
| • |
The quality, performance, and/or functions of this product will differ according to the conditions of use. Please contact our department in charge for full details of this product. |
| • |
Under severe conditions, this product may show difference between the sample observed values and the actual performance. Please test and evaluate the product thoroughly for your safety and better results. |
| • |
This product and/or its features may change or be discontinued without any prior notice. |
| • |
The intellectual property rights of this document belongs to Nitto Denko Corporation. Please contact our department in charge for usage not in accordance of the intended use. Copying and/or reproducing the document without notice are strictly prohibited. All rights reserved. |
|
|
|
|
|