| Ultra-Thin, Double-Coated Adhesive Tape |
|
| No.5601 |
 |
| Nitto Denko No.5601 double-coated tape with a thickness of only 0.01mm helps to reduce thickness of electronic devices.
Even in a limited space, this ultra-thin double-coated adhesive tape enables to fix various types of thin components.
|
|
Features |
|
| • |
An ultra-thin, double-coated adhesive tape using polyester film as the carrier material that realized a thickness of 0.01mm. |
| • |
Using polyester film as the carrier material, a superior uniformity of the tape thickness is realized in addition to its excellent processability and workability. |
| • |
Using polyester film release liner and plastic core, it hardly causes dust. |
|
Structure |
|
|
Properties |
|
| 180° peeling strength according to type of substrate [Unit: N/20mm] |
| Substrate |
Adhesive Strength |
| Stainless steel |
8.3 |
| Acrylic |
8.0 |
| Polycarbonate |
9.0 |
| Polyester |
7.8 |
|
| *Measured by peeling in 180° direction at a speed of 300mm/min. at 23°C with PET #25 backing. |
| 180° peeling strength according to temperature (stainless-steel) [Unit: N/20mm] |
| Test Temperature |
Adhesive Strength |
| 23°C |
8.3 |
| 40°C |
7.8 |
| 60°C |
6.2 |
| 80°C |
6.1 |
|
| *Measured by peeling in 180° direction at a speed of 300mm/min. with PET #25 backing,
Tape pressure application and measurement at temperatures given in the table above. |
|
Applications |
|
| • |
For fixing reflection sheets and film materials used for compact-size LCD backlight modules such as cellular phones. |
| • |
For fixing electromagnetic wave absorption sheets. |
| • |
For fixing film materials in compact-size electronic devices. |
* The above values are sample observed values, not the guaranteed performance.
* The applications given herein are suggested examples. Please make sure the product is capable of the application before actually attempting to put it to use. |
|
|
|
|
|